Seamless Steel Pipe manufacture in China Used for oil and gas transportation

0 Ratings P142-491241-49616

Price Range : USD 101 - USD 1000

Supplier : HUNAN GREAT STEEL PIPE CO., LTD

Product Details

Model No Normal
Make Great Pipe
Origin China
Unit Kilogram
Minimum Order Quantity 1000

Technical Specification / Description

Seamless Steel Pipe, Carbon Seamless Steel Pipe(CS), Stainless Seamless Steel Pipe(SS) and Other Pipe Fittings

Abundant Inventory +  Competitive Price

 

Top quality —— Hydralic Test, X-ray, Offer-line UT, Eddy Current Inspection, etc, 3rd party inspection to test.
Fast delivery —— Many sets of advanced production equipment to produce, as well as perfect logistics system.
Timely quotation —— professional sales quote for you after receive your inquiry.
Certificate share —— MTC, ISO, Inspection Report and other quality certification.
Used for oil and gas transportation, the general structure, mechanical structure.

 

 

Types of Seamless Steel Pipe

TypesUses
Structure PurposesGeneral structure and mechanical
Liquid ServicesPetroleum, gas and other fluids conveying
Low and Medium PressureSteam and boiler manufacturing
Hydraulic Pillar ServiceHydraulic support
Auto Semi-shaft CasingAuto sem-shaft casing
Line PipeOil and gas conveying
Tubing and CasingOil and gas conveying
Drill PipesWell drilling
Geological Drilling PipesGeological drilling
Petroleum Cracking TubesFurnace tubes, heat exchangers

 

1.jpg

Size: OD: 13.72-914.4mm / WT: 1.65-22mm,

Length: 0.5mtr-20mtr

 

Dimension Tolerances of Seamless Steel Pipe

Standard

Grade

Chemical Components (%)

Mechanical Properties

c

Si

Mn

P

S

Mo

Cr

V

Tensile STrength(Mpa)

Yield STrength(Mpa)

Elongation

(%)

ASTM A53

A

≤0.25

/

≤0.95

≤0.05

≤0.06

≤0.15

≤0.40

≤0.08

≥330

≥205

≥29.5

B

≤0.30

/

≤1.2

≤0.05

≤0.06

≤0.15

≤0.40

≤0.08

≥415

≥240

≥29.5

 

Standard

Grade

Chemical Components(%)

Mechanical Properties

c

Si

Mn

P

S

Mo

Cr

V

Tensile STrength

(Mpa)

Yield STrength

(Mpa)

 Elongation(%)

ASTM A106

A

≤0.30

≥0.10

0.29-1.06

≤0.035

≤0.035

≤0.15

≤0.40

≤0.08

≥415

≥240

≥30

B

≤0.35

≥0.10

0.29-1.06

≤0.035

≤0.035

≤0.15

≤0.40

≤0.08

≥485

≥275

≥30

 

Standard

Grade

Chemical Components(%)

Mechanical Properties

c

Si

Mn

P

S

Tensile STrength(Mpa)

Yield STrength(Mpa)

Elongation(%)

ASTM A179

A179

0.06-0.18

/

0.27-0.63

≤0.035

≤0.035

≥325

≥180

≥35

 

 

Standard

Grade

Chemical Components(%)

Mechanical Properties

c

Si

Mn

P

S

Tensile STrength(Mpa)

Yield STrength(Mpa)

Elongation(%)

ASTM A192

A192

0.06-0.18

≤0.25

0.27-0.63

≤0.035

≤0.035

≥325

≥180

≥35

 

 

Cold Drawing

The process of cold drawing is a procedure by which steel profiles are formed in order to achieve complex cross sections of excellent precision in these cold drawn steel shapes. After careful pre-treatment and de-scaling, the special profile bars are drawn through a forming die. This operation can be repeated up to three or four times. Cold drawing of hot rolled and hot extruded special pre-shape steel profiles tightens the cross-sectional tolerances, thus leading to significant improvement in dimensional accuracy and surface quality. Cold drawn steel special profiles offer the same precision achieved by machining but without the waste.

Hot Rolling

During the production of special hot rolled steel profiles by hot rolling the input billet or slab is formed into lengths up to 70 m using two oppositely rotating cylindrical rolls. The hot rolled steel shapes of this forming technique are used in a multitude of industrial applications. Hot rolled special profiles offer innovative solutions whether it be for automotive, materials handling, railroad or thicker flange and web thickness structural steel shapes use. Finished hot rolled steel shapes are roller straightened and sheared into production lengths or sawn into fixed lengths according to customer wishes.

Hot Extruding

During hot extrusion a round steel billet is pre-heated and, after leaving the furnace, is pushed through a forming die into a profile bar using a ram with an extrusion force of 2,200 ton. Hot extrusion offers substantial advantages in comparison to hot rolling forging or machining. Hot extrusion can be used to make complex profile shapes even using metals which are difficult to form. In addition, small lot sizes can be produced economically.

Cold Rolling  Cold Forming Roll Forming

Roll forming can be described as a continuous bending operation done at room temperature in which sheet or strip metal is plastically deformed along a linear axis. Tandem sets of rolls (known as roll stations) shape the metal stock in a series of progressive stages until the desired cross-sectional configuration is obtained by cold rolling.Roll forming is ideal for producing parts with long lengths or in large quantities. It can also produce multiple length parts from the same set of tooling. Virtually any material that can be cold formed by sheet forming techniques can be roll formed.

 